Influence of a nucleating agent on the crystallization behaviour of isotactic polypropylene and elastomer blends

The influence of a nucleating agent on the crystallization behaviour of isotactic polypropylene (iPP), in their blends with poly(styrene-b-ethylene butylene-b-styrene) (SEBS), and a metallocenic ethylene–octene copolymer (EO) was investigated by DSC, optical microscopy and real-time small and wide angle X-ray scattering (SAXS and WAXS) experiments using synchrotron radiation. In non-nucleated iPP/SEBS blends, the crystallization of the iPP matrix occurred in the presence of the styrenic domains which induced a nucleating effect on the process, as observed in the synchrotron experiments. The metallocenic elastomer did not affect the crystallization behaviour of iPP in the iPP/EO blends in non-isothermal experiments, however, the development of crystallinity in the elastomer was restricted. In the nucleated isotactic polypropylene/elastomer blends a significant increase in the crystallinity and the crystallization rate of the iPP matrix was observed due to the presence of the nucleating agent. However, the nucleating efficiency of the additive was strongly affected by the nature and content of the elastomeric component. The nucleating agent efficiency was higher in the presence of the ethylene–octene component than the styrenic elastomer.