Effect of tie-layer thickness on the adhesion of ethylene–octene copolymers to polypropylene

The adhesion of some ethylene–octene copolymers to polypropylene (PP) and high density polyethylene (HDPE) was studied in order to evaluate their suitability as compatibilizers for PP/HDPE blends. A one-dimensional model of the compatibilized blend was fabricated by layer-multiplying coextrusion. The microlayered tapes consisted of many alternating layers of PP and HDPE with a thin tie-layer inserted at each interface. The thickness of the tie-layer varied from 0.1 to 15 μm, which included thicknesses comparable to those of the interfacial layer in a compatibilized blend. The delamination toughness was measured in the T-peel test. Generally, delamination toughness decreased as the tie-layer became thinner with a stronger dependence for tie layers thinner than 2 μm. Inspection of the crack-tip damage zone revealed a change from a continuous yielded zone in thicker tie layers to a highly fibrillated zone in thinner tie layers. By treating the damage zone as an Irwin plastic zone, it was demonstrated that a critical stress controlled the delamination toughness. The temperature dependence of the delamination toughness was also measured. A blocky copolymer (OBC) consistently exhibited better adhesion to PP than statistical copolymers (EO). A one-to-one correlation between the delamination toughness and the reported performance of the copolymers as compatibilizers for PP/HDPE blends confirmed the key role of interfacial adhesion in blend compatibilization.