Poly(4-diphenylaminostyrene) with a well-defined polymer chain structure: Controllable optical and electrical properties

The effect of polymer chain structure on the optical and electrical properties are reported for poly(4-diphenylaminostyrene) (PDAS), which was prepared by the living anionic polymerization of 4-diphenylaminostyrene (DAS) with the benzyllithium (BzLi)/N,N,N′,N′-tetramethylethylenediamine (TMEDA) system. The optical properties of PDAS are strongly affected by the stereoregularity of the PDAS polymer chain; intramolecular excimer-forming fluorescence was observed from PDAS with a syndiotactic-rich configuration. The highest occupied molecular orbital (HOMO) and lowest unoccupied molecular orbital (LUMO) energy levels of PDAS were approximately −5.4 and −2.0 eV, respectively, regardless of the polymer chain structure. The hole and electron drift mobilities for PDAS were in the order of 10−4 to 10−5 (cm2/V s) and 10−5 (cm2/V s), respectively, with negative slopes. The distance of each triphenylamino (TPA) group in the polymer chain was a major factor influencing the drift mobility of PDAS. The current–voltage (I–V) characteristics of PDAS were controllable according to the polymer chain structure of PDAS.