The effect of type II collagen coating of chitosan fibrous scaffolds on mesenchymal stem cell adhesion and chondrogenesis

The biocompatibility of chitosan and its similarity to glycosaminoglycans (GAG) make it attractive for cartilage tissue engineering. We have previously reported improved chondrogenesis but limited cell adhesion on chitosan scaffolds. Our objectives were to produce chitosan scaffolds coated with different densities of type II collagen and to evaluate the effect of this coating on mesenchymal stem cell (MSC) adhesion and chondrogenesis. an fibrous scaffolds were obtained by a wet spinning method and coated with type II collagen at two different densities. A polyglycolic acid mesh served as a reference group. The scaffolds were characterized by Fourier-transform infrared spectroscopy, scanning electron microscopy (SEM), transmission electron microscopy (TEM) and type II collagen content. Constructs were analyzed after MSCs seeding via live/dead assay, weight and DNA evaluations, SEM, and TEM. Constructs were cultured in chondrogenic medium for 21 days prior to quantitative analysis (weight, DNA, and GAG), SEM, TEM, histology, immunohistochemistry, and quantitative real time polymerase chain reaction. The cell attachment and distribution after seeding correlated with the density of type II collagen. The cell number, the matrix production, and the expression of genes specific for chondrogenesis were improved after culture in collagen coated chitosan constructs. findings encourage the use of type II collagen for coating chitosan scaffolds to improve MSCs adhesion and chondrogenesis, and confirm the importance of biomimetic scaffolds for tissue engineering.