Magnetization anisotropy of Ni dots with several tens of nanometer diameter

We have studied the magnetization of Ni dot with 50 to 70 nanometer diameter and 12 nanometer thickness using a magnetic force microscopy with an in-plane magnetic field. The Ni dots were prepared using self-assembled dot patterns with poly (styrene-b-methyl mathacrylate) diblock copolymers on Ni film and ion etching. It was found that the remanent magnetization direction of the dot was perpendicular to the plane as prepared. From the vibrating sample magnetometer measurement, a hysteresis loop was found in the perpendicular magnetization. When an in-plane external magnetic field was applied, the magnetization was rotated into a horizontal direction with low coercivity along the field direction.