Synthesis of CoFe2O4 nanowire arrays by sol–gel template method

CoFe2O4 nanowire arrays with an average diameter of about 40 nm were prepared in porous anodic aluminum oxide (AAO) template using sol–gel process. Transmission electron microscopy (TEM) diffraction pattern and X-ray diffraction (XRD) showed that the nanowires were polycrystalline phase. Magnetic measurements showed the arrays of nanowires did not show a preferential magnetic orientation, the reason was briefly discussed. The effect of heating rate on the structure and magnetic properties of CoFe2O4 nanowire arrays was investigated. The result showed that the coercivity decreased with the increase of the heating rate.