Development of high efficiency nanofilters made of nanofibers

Electrospinning is a fabrication process that uses an electric field to control the deposition of polymer fibers onto a target substrate. This electrostatic processing strategy can be used to fabricate fibrous polymer mats composed of fiber diameters ranging from several microns down to 100 nm or less. In this study, optimized conditions to produce nanofibers using Nylon 6 are investigated and the Nylon 6 nanofilters using nanofibers of 80–200 nm in diameter are designed and evaluated the filtration efficiency and pressure drop across the filter. When the Nylon 6 concentration is 15 wt.%, electrospun fibers have an average diameter of 80 nm, but there are many beads, and the concentration increases to 24 wt.%, the fiber diameter gradually thickens to 200 nm, but there are not any beads. When the spinning distance is small, the thinner nanofibers are produced and the more fibers are collected on the grounded electrode. The filtration efficiency of Nylon 6 nanofilters is 99.993% superior to the commercialized HEPA filter at the face velocity of 5 cm/s using 0.3 μm test particles. Even though the high pressure drops across the nanofilter, they show the potential to have the application of HEPA and ULPA grade high efficiency filter.