Wettability of ultraviolet excimer-exposed PE, PI and PTFE films determined by the contact angle measurements

Effects of the exposure of ultraviolet (UV) excimer light on the physicochemical surface properties of polymer films were investigated by contact angle measurements and X-ray photoelectron spectroscopy (XPS). The UV light at wavelength of 172 nm was exposed to polyethylene (PE), polyimide (PI), and polytetrafluoroethylene (PTFE) films in ambient air. The advancing and receding contact angles of water on the unexposed and UV-exposed films were determined by the sessile drop and the Wilhelmy methods as a measure of the wettability. For the PE and PI films, remarkable decrease in the water contact angle was accomplished by the UV exposure of several or several 10 s. The XPS data showed that such increase in the wettability was attributed to the increased atomic oxygen concentration at the film surfaces. The wettability of the PTFE film did not change due to the UV exposure. When the UV-exposed PE and PI films were stored in ambient air, the increase in the water contact angle, i.e. the hydrophobic recovery, was observed over a time scale of several days. It was suggested that the gasification of the low-molecular weight oxidized materials as well as the reorientation and the migration of polymer chains in the oxidized surface layer was responsible for the hydrophobic recovery in air. The UV exposure was also attempted to the PI film being covered with a metal mesh to prepare the film having both non-exposed and UV-exposed surface regions. The differences in the advancing and receding contact angles between the both regions were observed on the continuous weight recording at constant interfacial moving velocity by the Wilhelmy method. The Wilhelmy method in combination with the UV lithography technique enabled the simultaneous evaluation of the wettabilities of the treated and untreated surfaces.