Dependence of high electric-field-induced strain on the composition and orientation of Pb(Mg1/3Nb2/3)O3–PbTiO3 crystals

Electric-field-induced strain behavior of (1−x)Pb(Mg1/3Nb2/3)O3–xPbTiO3 (PMNT) crystals with different orientations and compositions was investigated for use as electromechanical actuators. Crystallographically, high strains with low hysteresis were achieved for 〈001〉 oriented rhombohedral crystals (29%≤x≤31%) near a morphotropic phase boundary, rather than 〈110〉 and 〈111〉. Domain instability could explain inferior strain levels and large hysteresis for 〈110〉 and 〈111〉 oriented crystals. Ultrahigh strain levels up to 1.8% could be achieved for 〈001〉 oriented PMNT crystals, being related to an E-field induced phase transition. −2 kV/cm negative E-field can be applied to PMNT ferroelectric material with low hysteresis. High strain with low hysteresis makes PMNT crystals promising candidates for high performance solid-state actuators.