Effect of ambient air pressure on synthesis of copper and copper oxide nanoparticles by wire explosion process

Nanoparticles of copper and copper oxide were synthesized by wire explosion technique in the environment of different ambient air pressure. Copper wire with a diameter of 125 μm and 6.1 cm in length has been exploded in air at 1 bar, 500 mbar, 100 mbar and 50 mbar. Current density in the order of 106 A cm−2 has been applied to disintegrate the wire by discharging a 1.85 μF capacitor at 10 kV. It is found that the particle size distribution for nano-sized particles follows the log-normal distribution and the median diameter is found to decrease from 31.3 nm to 23.6 nm as the pressure is decreased from 1 bar to 50 mbar.