Magnetostriction relative to pretransition in Ni50.5Mn24.5Ga25 single crystal

The strain behaviors as well as the structural and magnetic changes relative to the pretransition in the Ni50.5Mn24.5Ga25 single crystals have been characterized by various methods, such as pretransition strain, magnetostriction, magnetization measurements, and TEM observations. A large magnetostriction up to 505 ppm measured in the [001] direction of the sample is obtained at the pretransition temperature with only a low magnetic field of about 1 kOe applied along the [010] direction. We found that not only the pretransition strain pronounces a more large change, but also the magnetostriction at a certain temperature exhibits a more large magnitude for field applied along the [010] direction than with field along the [001] direction. It is concluded that the magnetoelastic interaction is responsible for the premartensitic transition, and the magnetoelastic interaction in the [010] direction is stronger than that in the [001] direction.