High-temperature X-ray diffraction and Raman scattering studies of Ba-doped (Na0.5Bi0.5)TiO3 Pb-free piezoceramics

The structural changes in (100 − x)Na0.5Bi0.5TiO3–xBaTiO3 (0 ≤ x ≤ 10) ceramics were investigated as a function of composition and temperature by X-ray diffraction and Raman spectroscopy. As Ba concentration increases, the structure changed from rhombohedral to tetragonal (x ≥ 6.5) across a morphotropic phase boundary like phase coexistence at x ∼ 5.5, which is further evidenced by phonon anomalies observed in composition-dependent Raman spectra. On heating, the disappearance of peak splits in {111} (x ≤ 5) and {200} (x ≥ 6.5) Bragg peaks and the changes in their 2θ-positions indicated temperature-driven structural changes: ferroelectric to antiferroelectric (≈Td, depolarization temperature) at 220 °C and antiferroelectric to paraelectric (rhombohedral to tetragonal) at 320 °C. In addition, Raman spectral analysis suggested that at elevated temperatures, two tetragonal phases with slightly different space groups coexisted at x ≥ 6.5 and most of the phase transition temperatures shifted towards left with increasing x.