Evolution of structural and magnetic properties of FePt/C granular films with thermal annealing

We report the structural and magnetic properties of as-deposited and thermally annealed FePt/C granular multilayer films. The as-deposited system exhibits a disordered fcc FePt phase with an average grain size of 3 nm. Thermal annealing at 650 °C results in partial L 1 0 ordering and an associated grain growth to 7 nm. Mِssbauer measurements show that there is no non-magnetic component present, suggesting that carbon resides only in the grain boundary region. The ferromagnetic grains are magnetically decoupled.