Effect of TiO2 on the mechanical and adhesion properties of RTV silicone elastomer coatings

Silicone elastomer coatings (SEC) have been of interest for marine application due to their good surface properties. However, they suffer from low mechanical properties and poor adhesion to substrate. s work, the effect of the TiO2 content on the mechanical properties of a SEC, including tensile strength and modulus, hardness and abrasion resistance were studied. The effect of TiO2 on the adhesion strength of SEC top layer to a tie layer was also investigated and the results were correlated to the mechanical properties of SEC. sults revealed that the inclusion of TiO2 in the SEC affects various properties of the coatings. The extent of the effect, however, depends on the TiO2 loading. Tensile tests, initially, showed a relatively rapid increase of the modulus with TiO2 content. This was then followed by a decrease in modulus as TiO2 was further increased. ll-off test results showed an increase in the adhesion strength with increasing TiO2 up to 10 wt.%, beyond which, the trend was reversed. The former is assumed to be due to an increase in the cohesive strength of the coating while the later is attributed to a pigment accumulation and difficulty in its dispersion.