Nanostructures formations, electrical transitions and implanted impurity migration in α-alumina modified by Ti ion beam assisted W deposition and subsequent thermal annealing
Author/Authors :
Duvanov، نويسنده , , Sergei M and Kabyshev، نويسنده , , Alexander V and Balogh، نويسنده , , Adam G، نويسنده ,
Issue Information :
روزنامه با شماره پیاپی سال 2002
Abstract :
Concentration depth profiles of implanted impurities and surface microstructure of modified polycrystalline α-Al2O3 were studied in the vicinity of the post-implantation annealing temperature of 1380 °C where a transition to low-resistance state occurs. The modification procedure was Ti ion implantation with simultaneous deposition of W (IBAD) and subsequent isochronal annealing in vacuum at temperatures ranging from 900 to 1500 °C. Direct metal vapor vacuum arc pulsed implantation of Ti ions (50–150 keV, 1017 ions per cm2, RT) was used. This treatment of ceramics is of interest for both basic and applied research. On the scientific side, it is intended to elucidate the correlation between the physical properties of ceramics and their nanostructure. From the point of view of the applications, this treatment is promising for production of low-cost, high ohmic thin film resistors and advanced gradient thermally stable metal/ceramic interfaces. Rutherford backscattering spectrometry (RBS) of 4He+ ions with initial energy of 1.8 MeV was used to determine the concentration depth profiles of the implanted impurity in the Al2O3 matrix. Scanning electron microscopy was applied to surface microstructure studies of the ceramics. RBS spectra were measured from the alumina samples annealed at temperatures corresponding to the maximum of the sheet resistivity–annealing temperature curve. The effective diffusion coefficient of implanted Ti in Al2O3 was found to be 2.43×10−14 cm2 s−1 for a temperature range of 1150–1230 °C. Nanocrystalline grains with a typical diameter of approximately 40–50 nm were formed at all post-implantation annealing temperatures. These nanocrystallites agglomerate into larger particles, the latter forming a quasi-crystalline surface structure at approximately 1150 °C. The transition to the low resistance electric state in Al2O3 at the post-implantation annealing temperature of approximately 1380 °C occurs simultaneously with a redistribution of the implanted Ti ions towards the near-surface layer and with a formation of a 2D honeycomb (average structure unit is 330 nm in length) nanostructure like an infinite cluster. The grain growth depression observed at temperatures near or above 1150 °C is consistent with the assumption that a diffusion barrier of the W and Ti constituents is formed on the nanocrystallite surfaces.
Keywords :
Diffusion coefficient , Sheet resistivity , Thermal annealing , Polycrystalline ?-Al2O3 , Ti ion beam assisted W deposition , Depth profile
Journal title :
Surface and Coatings Technology
Journal title :
Surface and Coatings Technology