Study of the surface modification of a Nylon-6,6 film processed in an atmospheric pressure air dielectric barrier discharge

A Nylon-6,6 film has been treated using an atmospheric pressure air dielectric barrier discharge (DBD). The resultant surface modifications were studied using X-ray photoelectron spectroscopy (XPS), contact angle measurement and secondary ion mass spectrometry (SIMS). The surface oxidation arising in the DBD discharge was found to arise in two stages: in the first stage, the creation of the carbon sites singly bonded to oxygen is dominant, the second stage leads to further conversion of such lightly oxidised carbons to those more heavily oxidised. The marked increase found in the hydrophilicity of the surface post-treatment is in the main believed to be associated with the earlier outcome. Partial recovery of the surface contact angle values is found for the treated samples following extended storage in ambient air. The final contact angle obtained for the treated samples was ∼50°, still reduced significantly from that of 83.5° for the untreated material.