Influence of silica sol particle behavior on the magnesium anodizing process with different anions addition

Combining the processes of colloid chemistry and electrochemistry the anodic films were made in electrolytes with silica sol addition. Two basic electrolytes 1 M NaOH + 10 vol.% silica sol and 1 M Na2SiO3 +10 vol.% silica sol were chosen to investigate the silica sol particle behavior during the anodizing process. The anodic films were prepared separately in the two basic electrolytes with various Na2CO3 or Na3PO4 additions at 2 A/dm2, 20 °C for 10 min. The micro-images and element contents of the specimen were characterized by SEM and EDS. The results showed that some cracks appeared on the films by adding PO43− in both of the two basic electrolytes. And the films became compact and uniform with the addition of CO32− in Na2SiO3 basic solution. Moreover, the film average thickness decreased with adding anions. It can be confirmed that the sol particle adsorbing behavior in the solution was influenced by the amount of anionsʹ charges, size and structure.