Surface modifications of polycarbonate (PC) and acrylonitrile butadiene styrene (ABS) copolymer by treatment with atmospheric plasma

Two engineering thermoplastic polymers (polycarbonate, PC, and acrylonitrile butadiene styrene copolymer, ABS) were treated with atmospheric plasma torch using different treatment rates (1, 5 and 10 m/min). The modifications produced by the treatment were analysed by contact angle measurements, XPS, SEM and ATR-IR spectroscopy. Particular emphasis was placed on the ageing (up to 30 days) after atmospheric plasma treatment on both polymers. ower the atmospheric plasma treatment, the greater the wettability of the treated polymers. The decrease in water contact angle was mainly ascribed to a significant increase in oxygen content due to the formation of carboxylic and hydroxyl groups and a decrease in the carbon content on the polymer surfaces. After natural ageing, there was an increase in the water contact angle, although the values of the untreated polymer surface were never reached.