Fracture toughness measurements of plasma-sprayed thermal barrier coatings using a modified four-point bending method

In this study, the adhesion strength of thermal barrier coatings 8YSZ (ZrO2 + 8 wt.% Y2O3) deposited on NiCrAlY bond coats by atmospheric plasma spraying is investigated experimentally. A modified four-point bending specimen that can generate a single interface crack to facilitate the control of crack growth was adopted for testing. The fracture surfaces were examined using a scanning electron microscope. Images show that cracks are initiated along YSZ/NiCrAlY interfaces, then kink and grow uniformly within the YSZ layer. The load–displacement curves obtained indicate three distinct stages in crack initiation and stable crack growth. Based on a microstructural model, finite element analyses were performed to extract the bonding strength of the thermal barrier coatings. The fracture toughness of the plasma-sprayed 8YSZ coatings, in terms of critical strain energy release rate Gc, can be reliably obtained from an analytical solution or from a numerical simulation of the cracking process using compliance methods.