Synthesizing hydrogen from ammonia over Ru incorporated SiO2 type nanocomposite catalysts

In this study, Ruthenium incorporated SiO2 type nanocomposite catalysts were prepared for COx free hydrogen production by using one-pot hydrothermal synthesis procedure. Experiments which were carried out under the flow of pure ammonia (300 ml/min) presented that 86% ammonia conversion was obtained at 500 °C over the catalyst having Ru/Si molar ratio of 0.060. Using promoter in the preparation of catalyst enhanced the catalytic activity especially for the ones prepared at low ruthenium loadings. While the catalyst that was prepared at a Ru/Si molar ratio of 0.010 without promoter gave negligible activity at 500 °C, the promoted one gave 33% conversion at 500 °C and 73% at 600 °C. Experiments were also repeated with lower feed flow rate values of ammonia such as 60 ml/min and 5 ml/min. It was seen that catalyst prepared at a Ru/Si molar ratio of 0.010 with promoter gave conversion value over 80% at 400 °C under the feed flow rate of 5 ml/min.