Enhancement of the photoluminescence of CdSe quantum dots during long-term UV-irradiation: privilege or fault in life science research?

The present study describes an impressive enhancement of the photoluminescence (PL) intensity of low-temperature synthesized CdSe nanocrystals (75 °C) during long-term UV-irradiation. The integrated PL-intensity of CdSe core and CdSe/ZnS core/shell nanocrystals, dispersed in chloroform, enhanced about 3 and 6 times, respectively, during 9 h exposure to UV-light, without any significant changes in the characteristic absorbance spectra and shifting of PL-spectra. After termination of the irradiation a comparatively slow photobleaching was detected with τ1/2=6 h for CdSe core and τ1/2=14 h for CdSe/ZnS core/shell nanocrystals. The most impressive was the effect of UV-irradiation on the photoluminescence of water-soluble CdSe nanocrystals. The integrated PL-intensity enhanced about 10 times during 11 h exposure to UV-light and the improved PL-intensity was preserved during 3 days after termination of the irradiation without any significant photobleaching. The results are discussed in the context of application of CdSe nanocrystals as novel fluorophores in life science experiments.