Characterization of Physic nut (Jatropha curcas L.) shells

The characterization of Physic nut shells was done using the wet chemical analysis of wood components. The obtained fractions were analyzed using IR, NMR, GPC, ICP and MALDI-TOF mass spectroscopy. TGA was used to determine the fixed carbon (+ash) and water content of the shells. The results of wet chemical analysis of wood components offered a clear procedure to isolate the main components in Physic nut shells (a). The fractions obtained were: polar extract (b), non-polar extract (c), Acid Insoluble Lignin (d), Holocellulose (e), α-Cellulose (f). The total Lignin content present in the shells equaled 48.84%. IR and NMR spectroscopy demonstrated that the non-polar extract is Lignin, which corresponds to the extractable Lignin (1.24%) in the Physic nut shells and the Acid Insoluble Lignin was 47.60%. Elemental analysis showed no Sulfur present in the investigated materials. Furthermore both 1H and 13C NMR of the non-polar extract showed the presence of aliphatic hydrocarbon chains. The α-Cellulose content (22.29%) and the Hemicelluloses content (23.84%) were in line with that of agricultural residues. The water content and the fixed carbon content (+ash [2.8%]) equal 5–6% and 35.6%, respectively. GPC showed that the polydispersity of the non-polar extract (3.6) lies between Alcell Lignin and Kraft Lignin. The polar extract contains a variety of metals, with especially a high amount of the alkali metals K and Na. The extraction with water is proposed to generate a fertilizer fraction and may be applied to reduce potential sintering issues during eventual combustion or gasification of the shells.