An advanced method to manufacture hierarchically structured carbide-derived carbon monoliths

The preparation of carbide-derived carbon (CDC) monoliths with a hierarchically structure in the nm and μm range is presented. Basis is the manufacturing of porous cellular SiC ceramics based on a biomorphous approach with μm porosity and subsequent conformal conversion to CDC by reactive extraction with chlorine. The SiC ceramics can be sintered at low temperatures and short times (1500 °C, 2 h) compared to classical preparation methods. The SiC ceramics show a macro pore volume (1–10 μm channel size) of 0.56 ml g−1, which corresponds to 1.5 ml g−1 in the resulting CDC. The final carbon material exhibits an additional nano pore volume of 0.525 ml g−1 with a mean slit pore size of 0.86 nm. Mechanical stabilities of the highly porous CDC are excellent (bending strength 2.1 ± 0.2 MPa, corrected Weibull modulus 8.7, characteristic strength 2.2 MPa and Youngs modulus 10.0 ± 0.5 GPa). The reactive extraction of the carbide monoliths shows very high reaction rates, approx. two dimensions faster (95×) compared to non-porous samples. Thus the manufacturing of the structured carbide and CDC can be performed at lower costs.