The influence of calcination on the size of nanocrystals, porous structure and acid–base properties of mesoporous anatase used as catalytic support

Mesoporous anatase was prepared following sol–gel and using urea as template. The influence of calcination temperature on the phase stability, nanocrystal/aggregate size, pore size distribution and specific surface area as well as on the acid–base behavior in aqueous solutions was studied using X-ray diffraction, laser-Raman and diffuse reflectance spectroscopies, scanning electron microscopy and laser scattering as well as N2 adsorption–desorption isotherms and potentiometric mass titrations. ystal structure was kept constant upon calcination over the whole temperature range, 200–500 °C. In this range anatase is constituted from primary nanocrystals. These are assembled into larger, rather spherical, clusters of about 30–40 nm and then into aggregates of various sizes (0.2–0.3 μm and 2–100 μm) with a distribution centered at about 12 μm. Increase of the calcination temperature caused an increase in the size of the primary nanocrystals from 8.1 nm at 200 °C to 17.1 nm at 500 °C, whereas calcination does not influence the morphology at micro-scale. Moreover, increase of the calcination temperature from 200 °C to 500 °C brings about a shift in the mean pore diameter from 47 nm to 91 nm accompanied by a decrease in the specific surface area and pore volume. The above effects were related with the aforementioned increase in the size of the primary nanocrystals. The value of pzc and the values of surface charge determined at various pH do not practically depend on the calcination temperature. The absence of pore space confinement effects was explained in terms of the structure and size of the interface development between the anatase surface and the electrolytic solution.