Silver nanoparticles to self-assembled films: Green synthesis and characterization

In the present paper silver nanoparticle was synthesized by chemical reduction of silver nitrate by oxalic acid in aqueous solution. The nanoparticle film (self-assembled; mirror like illumination) on the wall of the clean glass surface was also observed after some days. The synthesized silver particles show an intense surface resonance plasmon band in the visible region at 425 nm. Transmission electron microscopy, selected areas electron diffraction, and UV–visible spectroscopy have been employed to characterize Ag-nanoparticles. The nanoparticle films were also observed using conventional visual and scanning electron microscope (spherical particles and size ranging from 23 to 245 nm). The transmission electron micrograph revealed that the average size of silver nanoparticle were ≤10 nm and 21–60 nm, respectively.