In situ sonosynthesis of nano TiO2 on cotton fabric

Here, titanium dioxide nanoparticles (NPs) were sonosynthesized and loaded simultaneously onto the cotton fabric. Titanium tetra isopropoxide (TTIP) was used as precursor and ultrasonic irradiation was utilized as a tool for synthesis of TiO2 in low temperature with anatase structure and loading nanoparticles onto the cotton fabric. TiO2 loaded cotton fabric was characterized by XRD, FE-SEM, EDS, and XRF. Moreover, several properties of the treated cotton fabrics such as self-cleaning, UV protection, washing durability, and tensile strength were studied. The effect of variables, including TTIP concentration and sonication time, was investigated based on central composite design (CCD) and response surface methodology (RSM). The results confirmed formation of anatase TiO2 nanoparticles with 3–6 nm crystalline size loaded onto the cotton fabric at low temperature (75 °C) that led to good self-cleaning and UV-protection properties. The excellent UV-protection rating of the treated fabric maintained even after 25 home launderings indicating an excellent washing durability. Interestingly, sonochemical method had no negative influence on the cotton fabric structure. The statistical analysis indicated significant effect of both TTIP concentration and sonication time on the content of the loaded TiO2 on the fiber and self-cleaning properties of the fabric.