Growth and scintillation properties of Pr doped YAP with different Pr concentrations

Pr3+ 0.2, 0.75, and 3 mol% doped YAP single crystalline scintillators were grown by using the micro-pulling down (μ-PD) method. Pr3+ 0.05 mol% doped YAP was also prepared by using the Czochralski method. In transmittance spectra, 4f–5d absorption line appeared at 230 nm. The μ-PD grown crystals showed intense emission at 290 nm while the Czochralski grown one showed an emission peak at 245 nm in radio luminescence spectra under X-ray excitation. Among them, the Czochralski grown one exhibited the highest light yield under 137Cs 662 keV excitation and the absolute light yield of this sample was estimated to be 20400±2000 ph/MeV. The decay time constants of these scintillators were around 10 ns due to Pr3+ 5d–4f transition.