Nikl، نويسنده , , M and Mares، نويسنده , , J.A and Chval، نويسنده , , J and Mihokova، نويسنده , , E and Solovieva، نويسنده , , N and Martini، نويسنده , , M and Vedda، نويسنده , , A and Blazek، نويسنده , , K and Maly، نويسنده , , P and Nejezchleb، نويسنده , , K and Fabeni، نويسنده , , P and Pazzi، نويسنده , , G.P and Babin، نويسنده , , K. Kalder، نويسنده , , K and Krasnikov، نويسنده , , A and Zazubovich، نويسنده , , S and D’Ambrosio، نويسنده , , C، نويسنده ,
Abstract :
Set of YAlO3:Ce single crystals co-doped with Zr4+ ions at concentrations of 0–200 ppm was characterized by photo-, radio- and thermo-luminescence, scintillation decay and light yield measurements. Positive influence of Zr co-doping was found, especially for the speed of scintillation response and lowering of TSL active traps.
Keywords :
YAlO3:Ce scintillator , radioluminescence , Scintillation decays , Zr4+ co-doping , Defect states , Thermostimulated luminescence