Active application improves the bonding performance of self-etch adhesives to dentin

Objectives luate the effect of application method on immediate and 6-month resin–dentin microtensile bond strength (μTBS) and nanoleakage (NL) of three one-step self-etch adhesives systems (Clearfil S3 Bond (S3), Xeno III (XE) and Adper Prompt L-Pop (AD)). s lusal enamel of 30 human molar was removed in order to expose a flat dentin surface. The adhesives were applied under two modes: inactive (IN) or active (AC) application. After light-curing (600 mW/cm2 for 10 s), composite buildups were constructed incrementally and sectioned to obtain bonded sticks (0.8 mm2) to be tested in tension immediately (IM) or after 6 months (6M) of water storage. For NL, three bonded sticks from each tooth at each time were coated with nail varnish, placed in silver nitrate and polished down with SiC paper. The μTBS data were submitted to a two-way ANOVA and Tukey’s test for each adhesive (α = 0.05). s showed higher μTBS to dentin when compared to IN in both periods of time (p = 0.001). Only for AD, lower μTBS was seen after 6M for IN and AC techniques. XE and S3 adhesives applied under IN showed a higher amount of silver penetration throughout the hybrid layer. Low silver nitrate deposition was seen for these adhesives under AC. After 6M, AD showed a higher amount of silver nitrate uptake under IN and AC techniques. sions roves the bonding performance of all one-step self-etch adhesive systems tested regardless of the time and this tendency was maintained over time.