Formation of nanoscale Fe/Ag multilayer by repeated press-rolling and its layer thickness dependence of magnetoresistance

We have successfully fabricated Fe/Ag multilayers that simultaneously possess the layer thickness of 4 nm and the layer number of above 10 000 by applying the repetition of pressing and rolling directly from a macroscopic stack of metal sheets. The clear correlation between the Ag layer thickness and MR ratio is observed, indicating that the critical layer thickness exhibiting magnetoresistance is 100 nm.