Rapid solidification of Cu–Fe–Ni alloys

Cu80−xNixFe20 (x=0, 5 and 20) alloys have been rapidly solidified by planar flow casting. X-ray diffraction (XRD) analysis of as-quenched ribbons shows bcc-Fe precipitates embedded in an fcc phase (x=0), two co-existing fcc solid solutions (x=5) and a complete solid solution of the parent elements (x=20). Thermal treatments in the temperature range between 400 and 600 °C give precipitation and spinodal decomposition reactions. These phase transformations have been evidenced from a variation of lattice constants, from a broadening of diffraction peaks and from TEM observations. The role of Ni content on competition between precipitation and decomposition reactions during rapid solidification and annealing is discussed in terms of thermodynamic arguments. Recent CALPHAD assessment of thermodynamic properties for Cu–Fe–Ni system has been used for an estimation of composition and volume fraction of equilibrium phases.