Foreign object damage in flexure bars of two gas-turbine grade silicon nitrides

Foreign object damage (FOD) behavior of two commercial gas-turbine grade silicon nitrides, AS800 and SN282, was determined at ambient temperature through strength testing of flexure test specimens impacted by steel ball projectiles with a diameter of 1.59 mm in a velocity range from 220 to 440 m/s. AS800 silicon nitride exhibited a greater FOD resistance than SN282, primarily due to its greater value of fracture toughness (KIc). The use of an additional equiaxed, fine-grained silicon nitride (NC132) showed that fracture toughness was a key material parameter affecting FOD resistance. The observed damages generated by projectile impact were typically in the forms of well- or ill-developed ring and cone cracks with little presence of radial cracks.