Tensile creep fracture of polycrystalline near-stoichiometric NiAl

Tensile creep fracture behavior of polycrystalline near-stoichiometric NiAl was studied between 700 and 1200 K under initial applied stresses varying between 10 and 200 MPa. The stress exponent for fracture varied between 5.0 and 10.7 while the activation energy for fracture was 250±22 kJ mol−1. The fracture life was inversely proportional to the secondary creep rate in accordance with the Monkman–Grant relation although there was extensive scatter in the data. This observation suggests that the fracture life for near-stoichiometric NiAl was influenced by creep under these stress and temperature conditions. Several different fracture morphologies were observed. Transgranular ductile cleavage fracture occurs at 700 K and at the higher stresses at 800 K. The fracture mode transitions to transgranular creep fracture at 900 and 1000 K and at lower stresses at 800 K, while plastic rupture and grain boundary cavitation occur at 1100 and 1200 K. An experimental fracture mechanism map is constructed for near-stoichiometric NiAl.