Composite films of nanostructured polyaniline with poly(vinyl alcohol)

The uniform composite films of nanostructured polyaniline (PANI) (e.g. nanotubes or nanorods with 60–80 nm in diameter) were successfully fabricated by blending with water-soluble poly(vinyl alcohol) (PVA) as a matrix. The PANI nanostructures were synthesized by a template-free method in the presence of β-naphthalene sulfonic acid (β-NSA) as a dopant. The molecular structures of PANI–β-NSA and the related composite films were characterized by UV–Vis absorption spectrum, FTIR spectrum and X-ray diffraction. It was found that the electrical, thermal and mechanical properties of the composite films were affected by the content of nanostructured PANI–β-NSA in the PVA matrix. The composite film with 16% PANI–β-NSA showed the following physical properties: room-temperature conductivity is in the range 10−2 S/cm, tensile strength ∼603 kg/cm2, tensile modulus ∼4.36×105 kg/cm2 and ultimate elongation ∼80%.