Polystyrene functionalized carbazole and electrochromic device application

Polystyrene (PS) functionalized carbazole macromonomer was synthesized and polymerized by electrochemical oxidative polymerization on the ITO-glass surface. The structure of the macromonomer was elucidated by 1H NMR, FT-IR, UV–Vis and cyclic voltammetry (CV). The spectro-electrochemical and electrochromic properties of the polymer film were investigated. Also the greenish blue colored film converted to dark blue color by the applying potential. Polystyrene-carbazole/polyethylenedioxythiophene (PS-Carb/PEDOT) electrochromic device was assembled in sandwich configuration: ITO-coated glass/anodically coloring polymer (PS-Carb)//gel electrolyte//cathodically coloring polymer (PEDOT)/ITO-coated glass. According to kinetic studies of this device, the optical contrast ΔT% at 640 nm between −1.0 and +2.0 V with a residence time of 10 s was found to be 38% and switching time was measured as 1.1 s.