Noda، نويسنده , , Shuji and Nagano، نويسنده , , Kazuhide and Inoue، نويسنده , , Eiji and Egi، نويسنده , , Toshio and Nakashima، نويسنده , , Takeshi and Imawaka، نويسنده , , Naoto and Kanayama، نويسنده , , Masahiro and Iwata، نويسنده , , Shiro and Toshima، نويسنده , , Kunihiro and Nakada، نويسنده , , Keiko and Yoshino، نويسنده , , Katsumi، نويسنده ,
Abstract :
The DSSC sub-module of 120 mm2 which has high temperature durability was fabricated. The durability was tested under 85 °C for 1000 h; at the end of the test the conversion efficiency was retained over 95% of the initial one. The high temperature durability was realized using the improved sealant, protective material of collecting grids and the new ruthenium-complex dye J2 which was developed by SIIT. By the same way the larger size module was developed.
Keywords :
solar cells , high temperature , durability , Module , Titania , Catalyst , Platinum , Screen-print , Dye-sensitized