A semi-continuous process for the synthesis of nanosize TiO2 powders and their use as photocatalysts

A semi-continuous process has been developed for the synthesis of TiO2 powders: a sol-gel reaction, using titanium isopropoxide as precursor and acetylacetone as chelating agent, followed by supercritical drying is performed. tained powders have been characterized by X-ray diffraction, SEM, TEM, BET method and OH surface groups measurements. The recovered solids are always crystallized in the anatase structure with particle size ranging from 8 to 13 nm. Surface area and OH surface groups density are around 100 m2·g−1 and 0.6 × 10−3 mol·g−1 respectively. otocatalytic activity of the elaborated powders has been studied following the degradation of phenol and compared to that of two commercial powders (P25 Degussa and Acros).