Superplastic behavior of a TiAl alloy in its as-cast state

Superplastic behavior of a TiAl alloy was investigated in a temperature range between 800 and 1000°C and at a strain rate of 1×10−4 s−1. The results show that the present alloy possesses very good superplasticity even in its as-cast state. A tensile elongation of 628% was obtained at 850°C. The observed superplastic behavior can be explained by the formation of a fine microstructure containing a metastable β-phase during solidification.