Author/Authors :
Leo، نويسنده , , G. and Chushkin، نويسنده , , Y. and Luby، نويسنده , , S. and Majkova، نويسنده , , E. and Kostic، نويسنده , , I. and Ulmeanu، نويسنده , , M. and Luches، نويسنده , , A. and Giersig، نويسنده , , M. and Hilgendorff، نويسنده , , M.، نويسنده ,
Abstract :
Colloidal Co particles of 11 nm diameter were deposited on Si substrate by spin coating and/or casting in magnetic field. A perpendicular magnetic field varying along the diagonal of the substrate was also applied. The samples were analyzed by transmission electron microscopy (TEM), field emission gun scanning electron microscopy (SEM-FEG), atomic and magnetic force microscopy (AFM/MFM). TEM micrographs show local order when a Co nanoparticle monolayer is deposited on Si. Drying the colloidal solution in a magnetic field leads to the formation of quite large clusters (0.3 μm) of Co nanoparticles. A stripe structure was then observed when the particles were deposited by casting in the varying magnetic field. AFM/MFM measurements show isolated Co clusters on the stripes. Magnetic features corresponding to the single Co cluster have been observed pointing out that all magnetic moments in the cluster are oriented along the field direction.