Double electrodeposition and heat treatment process for the fabrication of superconducting oxides on the intensified {1 1 3} <1 2 1> Ag substrate

The Tl-1223 coated conductor (Tl0.8Pb0.2Bi0.2Sr1.8Ba0.2Ca2.2Cu3Oδ) was synthesized by using electrodeposition on the intensified {1 1 3} <1 2 1> Ag substrate applying the new method of the repeating electrodeposition/heat treatment. The films were fabricated conducting the first electrodeposition and then heat treatment, after that the second electrodeposition on the first electrodeposition/heat treatment coated conductors. The second electrodeposition on the first electrodeposition/heat treatment/the first electrodeposition/heat treatment coated conductor showed the better quality of the Tl-1223 phases than that of the first electrodeposition/heat treatment coated conductor, showing more compact and dense grains on the films. The thin Tl-1223 films caused by the thinning process were discussed by considering the properties of Tl and the epitaxial growth aspects. The purer Tl-1223 grains obtained at the double electrodeposition/heat treatment are due to the growth from Tl-1223 grains already synthesized during the first electrodeposition/heat treatment, facilitating the epitaxial growth easier than that of the Ag substrate. The second electrodeposition process was successfully performed, obtaining 1.9 × 105 A/cm2 of Jc at 0 T at 10 K.