Lifetime obtained by ion beam assisted deposition

We have fabricated green organic light-emitting diodes based on tris-(8-hydroxyquinoline)aluminium (Alq3) thin films. In order to favor the charge carriers transport from the anode, we have deposited a N,N′-diphenyl-N,N′-bis (3-methylphenyl)-1,1′-diphenyl-4,4′-diamine (TPD) layer (hole transport layer) on a ITO anode. Cathode is obtained with a calcium layer covered with a silver layer. This silver layer is used to protect the other layers against oxygen during the OLED use. All the depositions are performed under vacuum and the devices are not exposed to air during their realisation. er to improve the silver layer characteristics, we have realized this layer with the ion beam assisted deposition process. The aim of this process is to densify the layer and then reduce the permeation of H2O and O2. We have used argon ions to assist the silver deposition. e OLEDs optoelectronic characterizations (I = f(V), L = f(V)) are performed in the ambient air. We compare the results obtained with the assisted layer with those obtained with a classical cathode realized by thermal unassisted evaporation. We have realized lifetime measurements in the ambient air and we discuss about the assisted layer influence on the OLEDs performances.