One-step through-mask electrodeposition of a porous structure composed of manganese oxide nanosheets with electrocatalytic activity for oxygen reduction

Potentiostatic electrolysis of a mixed aqueous solution of Bu4NBr and MnSO4 at +1.0 V (vs. Ag/AgCl) on Pt electrode led to the oxidation of Br− and Mn2+ ions. X-ray photoelectron spectroscopy (XPS), atomic force microscopy (AFM), and X-ray diffraction (XRD) revealed that this anodic process was followed by the deposition of insulating crystals of bromide salt of Bu4N+ and the subsequent formation of layered manganese oxide in the interstitial spaces of the bromide grains already grown. Dissolution of the bromide crystals in water left a well-dispersed porous texture composed of manganese oxide nanosheets. The resulting MnOx-modified electrode exhibited a larger catalytic current for the reduction of oxygen in alkaline solution, compared to the bare Pt electrode.