Dielectric properties of lead indium niobate ceramics synthesized by conventional solid state reaction method

Pyrochlore free lead indium niobate ceramics are successfully prepared using wolframite precursor by conventional solid state reaction method in air atmosphere, by adding an excess amount of MgO in PbO-InNbO4 mixture. The dielectric properties of lead indium niobate ceramic studied as a function of both temperature and frequency indicate relaxor ferroelectric behavior with maximum dielectric constant of 4310 at 40 οC for 1 kHz. Lowering of transition temperature and enhancement of dielectric constant at room temperature, compared to earlier reports, may be due to the diffusion of magnesium ion into the lead indium niobate. The saturation polarization Ps, measured at room temperature, is found to be 22.5 μC/cm2 for 40 kV/cm.