Piezoelectric and dielectric properties of 0.98(Na0.5K0.5)NbO3–0.02Ba(ZrxTi(1−x))O3 ceramics

Lead-free 0.98(Na0.5K0.5)NbO3–0.02Ba(ZrxTi(1−x))O3 (0.98NKN–0.02BZT) ceramics with Zr contents were fabricated by a conventional mixed-oxide method. The results indicate that the Zr/Ti ratio significantly influences the structural, piezoelectric, dielectric, and ferroelectric properties of 0.98NKN–0.02BZT ceramics. For the 0.98NKN–0.02BZT (x = 0) ceramics sintered at 1090 °C, the bulk density increased as the Zr contents decreased and showed a maximum value at x = 0. The Curie temperature of the 0.98NKN–0.02BZT ceramics slightly decreased as the Zr contents increased. The dielectric constant, piezoelectric constant, and electromechanical coupling factor of samples were maximized at x = 0, which might be due to the increase in density. A high d33 = 194 pC/N, kp = 38% were obtained for the 0.98NKN–0.02BZT ceramics sintered at 1090 °C for 4 h.