The effect of alkali metal on the surface properties of potassium doped Au-Beta zeolites

Beta zeolite was applied as support for gold introduced by gold-precipitation method and potassium added by impregnation or adsorption. The effect of zeolite composition and the amount of potassium introduced on the surface properties of the final materials was considered. Moreover, the interaction of gold and potassium species was found to be related to the adsorptive and catalytic behaviour of zeolites in NO reduction with propene and deodorization. K/Au-Beta(Impregnated) exhibits the best performance in the above mentioned processes because of the small gold particles (between 2 and 5 nm) and interaction of gold with potassium species leading to the change of electronic properties of the surface (the appearance of cationic gold species). Potassium added as a promoter improves the catalytic properties of Au-zeolite in N2O decomposition and also in deodorization (increase of the ability to dibutyl sulphide oxidation). The catalysts prepared were characterized by XRD, XPS, UV–vis, TEM, pyridine adsorption combined with FTIR and test reaction (2-propanol transformation).