Single crystalline multi-petal Cd nanoleaves prepared by thermal reduction of CdO

Multi-petal cadmium metal nanoleaves with 30–40 nm thickness were fabricated on abraded copper substrate by simple thermal reduction of cadmium oxide (CdO) powder at 1050 °C inside horizontal tube furnace (HTF) under nitrogen gas flow. The structural, compositional and morphological characterizations of the as-prepared cadmium nanoleaves (CdNLs) were performed by X-ray diffraction, energy dispersive X-ray spectroscopy, scanning electron microscopy, high resolution transmission electron microscopy and selected area electron diffraction. Non-catalytic vapour–solid (VS) process based growth mechanism governing the formation of CdNLs has been proposed and discussed briefly. Photoluminescence (PL) spectrum for CdNLs measured at room temperature exhibited a single prominent emission band at 353 nm which may either be ascribed to surface oxidation effects or interband radiative recombination under Xe light illumination.