Sonochemical and hydrothermal synthesis of PbTe nanostructures with the aid of a novel capping agent

In this work, a new Schiff-base compound derived from 1,8-diamino-3,6-dioxaoctane and 2-hydroxy-1-naphthaldehyde marked as (2-HyNa)-(DaDo) was synthesized, characterized, and then used as capping agent for the preparation of PbTe nanostructures. To fabricate PbTe nanostructures, two different synthesis methods; hydrothermal and sonochemical routes, were applied. To further investigate, the effect of preparation parameters like reaction time and temperature in hydrothermal synthesis and sonication time in the presence of ultrasound irradiation on the morphology and purity of the final products was tested. The products were analyzed with the aid of SEM, TEM, XRD, FT-IR, and EDS. Based on the obtained results, it was found that pure cubic phased PbTe nanostructures have been obtained by hydrothermal and sonochemical approaches. Besides, SEM images showed that cubic-like and rod-like PbTe nanostructures have been formed by hydrothermal and sonochemical methods, respectively. Sonochemical synthesis of PbTe nanostructures was favorable, because the synthesis time of sonochemical method was shorter than that of hydrothermal method.