Synthesis, Structural analysis, Mechanical, antibacterial and Hemolytic activity of Mg2 + and Cu2 + co-substitutions in β-Ca3(PO4)2

The present study reports the synthesis, structural, mechanical and in vitro characterization of a series of Mg2 + and Cu2 + co-substitutions in β-Ca3(PO4)2. Aqueous precipitation technique ensured the formation of calcium deficient apatite with substituted ions in the as prepared conditions and their subsequent heat treatments at 1000 °C resulted in the formation of crystalline β-Ca3(PO4)2. The combined substitutions of lower sized Mg2 + and Cu2 + in the structural lattice of β-Ca3(PO4)2 led to the significant contraction in a = b-axis and c-axis lattice parameters of β-Ca3(PO4)2. The results from Rietveld refinement confirmed the occupancy of Mg2 + and Cu2 + at the Ca(5) site of β-Ca3(PO4)2. The results from mechanical tests proved that Mg2 + and Cu2 + substitutions are not hindering the mechanical properties of β-Ca3(PO4)2. The antibacterial and hemolytic results determined for the Mg2 + and Cu2 + co-substituted β-Ca3(PO4)2 ensured their good activity against the investigated microbes and also confirmed their blood biocompatibility.