Structural and electric characteristics of (Na0.5Bi0.5)0.50Ba0.50TiO3 and (Na0.5Bi0.5)0.20Ba0.80TiO3 ceramics

(Na0.5Bi0.5)0.50Ba0.50TiO3 and (Na0.5Bi0.5)0.20Ba0.80TiO3 ceramics have been prepared by the solid state reaction and studied by X-ray diffraction and by measurements of dielectric and ferroelectric properties between room temperature and 550 °C. A sharp increase in the electric permittivity and dielectric loss near 212 °C (for the first material) and near 205 °C (for the second material) on heating with remarkable thermal hysteresis have been observed. This sharp increase in dielectric responses indicates transformation between normal and relaxor ferroelectric states. The X-ray diffraction study shows that this transformation corresponds to the first order phase transition from tetragonal to cubic. It was shown that polar regions can exist in higher temperatures in both materials. Also the use of both ceramics for device application has been indicated.