Mechanical alloying of MoSi2 with ternary alloying elements.: Part 1: Experimental

Phase evolution during the mechanical alloying of Mo and Si elemental powders with a ternary addition of Al, Mg, Ti or Zr was monitored using X-ray diffraction. Rietveld analysis was used to quantify the phase proportions. When Mo and Si are mechanically alloyed in the absence of a ternary element, the tetragonal C11b polymorph of MoSi2 (t-MoSi2) forms by a self-propagating combustion reaction. With additional milling, the tetragonal phase transforms to the hexagonal C40 structure (h-MoSi2). The mechanical alloying of Al, Mg and Ti additions with Mo and Si tend to promote a more rapid transformation of t-MoSi2 to h-MoSi2. In high concentrations, the addition of these ternary elements inhibits the initial combustion reaction, instead promoting the direct formation of h-MoSi2. The addition of Zr tends to stabilise the tetragonal phase.